Alkyd hull paint

It is composed of a modified alkyd resin, a coloring pigment, a drier, an auxiliary agent, a solvent, and the like.
Retail price
0.0
Market price
0.0
Number of views:
1008
Product serial number
Quantity
-
+
Stock:
0
1
产品描述

55

product manual
It is composed of a modified alkyd resin, a coloring pigment, a drier, an auxiliary agent, a solvent, and the like. Excellent product construction performance, high gloss film and good decorative performance.
Product Usage
Applicable to the hull and superstructure of ships above the waterline, as well as the use of onshore steel structures for topcoats.
Physical characteristics

colour Various colors
Volume solids 48±3% 
Dry film thickness 35mm
Wet film thickness 75mm
Theoretical dosage 0.090kg/m2 @35mm  
Drying time (23±2℃)
Dry ≤ 4h
Hard work ≤24h
Recommended number of coatings
2 channels, dry film thickness 70μm
Front paint
Various types of alkyd antirust paint.
Surface treatment
The front paint film must be dry.
Remove all dirt such as oil and dust from the paint film on the front, and there is no acid or alkali and moisture condensation on the paint film.
Construction instructions
The mixing ratio One-component, fully stirred by mechanical stirring
Thinner Alkyd thinner

Construction method

Painting method

Brushing, roller coating (applicable)

Air spray (applicable)

Airless spray (recommended)

Dilution rate

0%-3%

0%-10%

0-5%

Airless spraying: ejection pressure: 15-17MPa
Nozzle diameter: 0.38-0.43mm
Air spray: Adjust the viscosity with the matching diluent: 25-30S (coating -4/23 ± 2 °C)
Recoat interval

Construction temperature

5℃

20℃

30℃

Minimum recoating time

36h

24h

16h

Maximum recoating time

Unlimited*

* When the paint film is exposed for too long outdoors, it will adversely affect the adhesion of the heavy coating. Therefore, the surface of the paint film must be roughed, sanded or high-pressure fresh water rinsed to maintain sufficient interlayer adhesion during recoating. .
Tool cleaning
All tools must be cleaned with thinner after use.
Safety
Use this product with care. Please refer to the MSDS of this product before starting work.
Please pay attention to the safety precautions on the packaging label before and during use. In addition, the safety regulations prescribed by the relevant national or local government should also be observed.
Personal protection includes, but is not limited to, lung, eye and skin protection. If swallowed or otherwise in contact with this product, seek immediate medical attention. Precautions must be taken to prevent fire, explosion and environmental protection.

Construction Notes
The construction site shall be protected from open flames and may only be constructed in a well ventilated condition. Strong ventilation is required in applications where it is confined or where air is not circulating.
Air humidity: When the relative humidity of the air is greater than 80%, construction is not recommended.
Ambient temperature: When the ambient temperature is below 5 °C or above 40 °C, construction is not recommended.
Surface temperature of the substrate: When the surface temperature of the steel is lower than the dew point temperature of 3 °C, the construction is not recommended. If the surface temperature of the steel is too high, the surface of the paint film will be defective. Therefore, when the surface temperature of the steel is higher than 50 °C, the construction conditions should be adjusted and it will be noon. The construction will be moved to the morning and evening, or the awnings will be erected or moved to the workshop.
Other aspects: There should be good ventilation during construction. When painting, it should prevent the surrounding environment from causing pollution to the paint film, such as sandblasting and paint fog lamps. Avoid construction in the case of rain, snow, fog, sandstorms, and stop construction in areas with strong winds or high pollution. Excessive ventilation will cause the coating to dry too quickly and the paintability of the coating will deteriorate, and a large amount of pollutants ( Such as sand, salt particles, corrosion deposits) will cause the film properties to deteriorate, and the loss will increase.

Scan the QR code to read on your phone
We could not find any corresponding parameters, please add them to the properties table

Our professional production and development of high performance heavy anti-corrosion coating

Widely used in petrochemical, marine engineering, engineering machinery, various types of ships, steel structures, bridges, wind power facilities, containers, etc., supplemented by floor coatings, fireproof coatings, temperature-resistant coatings, interior and exterior wall coatings, etc. .